優質碳素結構鋼的牌號和化學成分
|
序號 |
統一數字 代號 |
牌號 |
化學成分(質量分數)(％) | |||||
|
C |
Si |
Mn |
Cr |
M |
Cu | |||
|
≤ | ||||||||
|
1 |
U20080 |
|
0.05-0.11 |
≤0.03 |
0.25-0.50 |
0.10 |
0.30 |
0.25 |
|
2 |
U |
|
0.07-0.13 |
≤0.07 |
0.25-0.50 |
0.15 |
0.30 |
0.25 |
|
3 |
U20150 |
|
0.12-0.18 |
≤0.07 |
0.25-0.50 |
0.25 |
0.30 |
0.25 |
|
4 |
U20082 |
08 |
0.05-0.11 |
0.17-0.37 |
0.35-0.65 |
0.10 |
0.30 |
0.25 |
|
5 |
U20102 |
l0 |
0.07-0.13 |
0.17-0.37 |
0.35-0.65 |
0.15 |
0.30 |
0.25 |
|
6 |
U20152 |
15 |
0.12-0.18 |
0.17-0.37 |
0.35-0.65 |
0.25 |
0.30 |
0.25 |
|
7 |
U20202 |
20 |
0.17-0.23 |
0.17-0.37 |
0.35-0.65 |
0.25 |
0.30 |
0.25 |
|
8 |
U20252 |
25 |
0.22-0.29 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
9 |
U20302 |
30 |
0.27-0.34 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
10 |
U20352 |
35 |
0.32-0.39 |
0.17-0.37 |
0.50-0.B0 |
0.25 |
0.30 |
0.25 |
|
11 |
U20402 |
40 |
0.37-0.44 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
12 |
U20452 |
45 |
0.42-0.50 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
13 |
U20502 |
50 |
0.47-0.55 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
14 |
U20552 |
55 |
0.52-0.60 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
15 |
U20602 |
60 |
0.57-0.65 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
16 |
U20652 |
65 |
0.62-0.70 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
17 |
U20702 |
70 |
0.67-0.75 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
18 |
U20752 |
75 |
0.72-0.80 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
19 |
U20802 |
80 |
0.77-0.85 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
20 |
U20852 |
85 |
0.82-0.90 |
0.17-0.37 |
0.50-0.80 |
0.25 |
0.30 |
0.25 |
|
21 |
U21152 |
15№ |
0.12-0.18 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.30 |
0.25 |
|
22 |
U21202 |
20Mn |
0.17-0.23 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.30 |
0.25 |
|
23 |
U21252 |
25Mn |
0.22-0.29 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.30 |
0.25 |
|
24 |
U21302 |
30Mn |
0.27-0.34 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.30 |
0.25 |
|
25 |
U21352 |
35Mn |
0.32-0.39 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.30 |
0.25 |
|
26 |
U21402 |
40Mn |
0.37-0.44 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.30 |
0.25 |
|
27 |
U21452 |
45Mn |
0.42-0.50 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.30 |
0.25 |
|
28 |
U21502 |
50Mn |
0.48-0.56 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.30 |
0.25 |
|
29 |
U21602 |
60Mn |
0.57-0.65 |
0.17-0.37 |
0.70-1.00 |
0.25 |
0.30 |
0.25 |
|
30 |
U21652 |
65Mn |
0.62-0.70 |
0.17-0.37 |
0.90-1.20 |
0.25 |
0.30 |
0.25 |
|
|
U21702 |
70Mn |
0.67-0.75 |
0.17-0.37 |
0.90-1.20 |
0.25 |
0.30 |
0.25 |
注：
1．表中所列牌號為優質鋼。如果是高級優質鋼，在牌號后面加“A”(統一數字代號最后一位數字改為“
2．使用廢鋼冶煉的鋼允許含銅量不大于0.30％。
3．熱壓力加工用鋼的銅含量應不大于0.20％。
4．鉛浴淬火(派登脫)鋼絲用的35.85鋼的錳含量為0.30％-0.60％；鉻含量不大于0.10％，鎳含量不大于0.15％，銅含量不大于0.20％；硫、磷含量應符合鋼絲標準要求。
5．08鋼用鋁脫氧冶煉鎮靜鋼，錳含量下限為0.25％，硅含量不大于0.03％，鋁含量為0.02％-0.07％。此時鋼的牌號為
6．冷沖壓用沸騰鋼含硅量不大于0.03％。
7．氧氣轉爐冶煉的鋼其含氮量應不大于0.008％。供方能保證合格時，可不做分析。
8．經供需雙方協議，08-25鋼可供應硅含量不大于0.17％的半鎮靜鋼，其牌號為08b-25b。
9．上述各成分含量皆指質量分數。